Type 403 S40300 - ASTM A580/A580M-2018

牌号	Type 403
美国UNS	S40300
对应标准	ASTM A580/A580M-2018 不锈钢丝 Stainless Steel Wire
归类	马氏体不锈钢

Type 403 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr
最小值	-	-	-	-	-	11.5
最大值	0.15	0.5	1	0.04	0.03	13

碳当量计算

Type 403 机械性能

条件	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	断面收缩率 ψ %	硬度 HBW
A	冷精轧	≥485	≥275	≥16	≥45
A	退火	≥485	≥275	≥20	≥45
T	冷精轧	≥690	≥550	≥12	≥40
H	冷精轧	≥830	≥620	≥12	≥40
t≤9.5mm	955℃，空冷					HRC ≥35

注1：Condition A —— Annealed as a final heat treatment.
Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength.
Condition T —— Heat treated to an intermediate temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
Condition H —— Heat treated to a hard temper generally by austenitizing, quenching, and tempering at a relatively low temperature.

1 近似对照表马氏体不锈钢

中国		中国台湾	日本	韩国	美国		俄罗斯	瑞典	英国
GB	ISC	CNS	JIS	KS	ASTM	UNS	GOST	SS	BS EN/BS
12Cr12 (1Cr12)	S40310	403	SUS 403	STS 403	403	S40300	08Х13	2301	403S17

2 近似对照表马氏体不锈钢

中国	日本	美国		德国	法国	欧标		俄罗斯	瑞典	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	NF EN/NF	EN	数字牌号	GOST	SS	BS EN/BS
0Cr13	SUS410S	410S Type403	S41008	X7Cr14	Z6C13 Z8C12	X6Cr13	1.4000	08KH13	2301	403S17

材料牌号对应供应商

告诉我在“材数库”看到，将给您优惠

上海亚螺精密紧固技术有限公司

主营: 各类不锈钢紧固件各类合金钢紧固件特殊材质紧固件螺塞/堵头耐高温不锈钢紧固件 A4-80螺栓

联系人：徐海
移动电话： 18621311857
电话：021-59766477

询价

江苏德镍金属科技有限公司

主营: 奥氏体不锈钢马氏体不锈钢沉淀硬化钢双相不锈钢高温合金钛合金汽轮机钢

联系人：郑经理
移动电话： 17365312205
微信号：17365312205

板材、薄板、带材、棒材、管材、型材等

询价

注：数据仅供参考！如有疑问，请填写"我要纠错"！