Type 403 S40300 - ASTM A580/A580M-2018

牌号	Type 403
美国UNS	S40300
对应标准	ASTM A580/A580M-2018 不锈钢丝 Stainless Steel Wire
归类	马氏体不锈钢

Type 403 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr
最小值	-	-	-	-	-	11.5
最大值	0.15	0.5	1	0.04	0.03	13

碳当量计算

Type 403 机械性能

条件	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	断面收缩率 ψ %	硬度 HBW
A	冷精轧	≥485	≥275	≥16	≥45
A	退火	≥485	≥275	≥20	≥45
T	冷精轧	≥690	≥550	≥12	≥40
H	冷精轧	≥830	≥620	≥12	≥40
t≤9.5mm	955℃，空冷					HRC ≥35

注1：Condition A —— Annealed as a final heat treatment.
Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength.
Condition T —— Heat treated to an intermediate temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
Condition H —— Heat treated to a hard temper generally by austenitizing, quenching, and tempering at a relatively low temperature.

1 近似对照表马氏体不锈钢

中国		中国台湾	日本	韩国	美国		俄罗斯	瑞典	英国
GB	ISC	CNS	JIS	KS	ASTM	UNS	GOST	SS	BS EN/BS
12Cr12 (1Cr12)	S40310	403	SUS 403	STS 403	403	S40300	08Х13	2301	403S17

2 近似对照表马氏体不锈钢

中国	日本	美国		德国	法国	欧标		俄罗斯	瑞典	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	NF EN/NF	EN	数字牌号	GOST	SS	BS EN/BS
0Cr13	SUS410S	410S Type403	S41008	X7Cr14	Z6C13 Z8C12	X6Cr13	1.4000	08KH13	2301	403S17