基本信息
牌号 A841 Grade B Class 1
对应标准 ASTM A841/A841M-2017
通过热机械控制工艺生产的压力容器用钢板
Steel Plates for Pressure Vessels, Produced by Thermo-Mechanical Control Process (TMCP)
归类 合金钢
化学成分
A841 Grade B Class 1 化学元素成分含量(%)
  成分 C Si Mn ① P S Cr Ni Cu Mo V Nb Al ② 更多
t≤40mm 最小值 - 0.15 0.7 - - - - - - - - 0.02 Alt≥0.02或Als≥0.015
最大值 0.15 0.5 1.35 0.03 0.025 0.25 0.6 0.35 0.3 0.06 0.03 -
  成分 C Si Mn P S Cr Ni Cu Mo V Nb Al ② 更多
t＞40mm 最小值 - 0.15 1 - - - - - - - - 0.02 Alt≥0.02或Als≥0.015
最大值 0.15 0.5 1.6 0.03 0.025 0.25 0.6 0.35 0.3 0.06 0.03 -
① Manganese may exceed 1.35 % on heat analysis, up to a maximum of 1.60 %, provided that the carbon equivalent on heat analysis does not exceed 0.47 %, or the value specified in Supplementary Requirement S77 when that requirement is invoked, when based on the following formula：
CE = C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15%
When this option is exercised, the manganese content on product analysis shall not exceed the heat analysis content by more than 0.12 percentage points.
② By agreement, the steel may be produced with titanium, in which case the minimum aluminum content shall not apply. When this option is exercised, the titanium content, by heat analysis, shall be .006 % to 0.02 %, and the actual titanium content shall be reported on the test report.
碳当量计算
机械性能
A841 Grade B Class 1 机械性能
抗拉强度
σb
Mpa 		屈服点
σs
Mpa 		断后伸长率或延伸率
δ
%
t≤65 485~620 ≥345 L0=50mm
≥22
t＞65 450~585 ≥310 L0=50mm
≥22
L0-标距
基本信息
接近匹配牌号 压力容器钢板1
# 标准 牌号(等级/别名/符号) 化学成分，重量%，最大值，除非另有说明
C Si Mn P S Cr Ni Mo Cu Al Ti V
热处理
1 ASME SA-662/SA-662M-2023 SA662M Grade B
0.220.13-0.450.79-1.620.0250.025-------
 -
2 ASME SA-662/SA-662M-2023 SA662M Grade C
0.240.13-0.550.92-1.720.0250.025-------
 -
3 ASTM A 662-2017(R2024) A662 Grade B
0.190.15-0.40.85-1.50.0250.025-------
 -
4 ASTM A 662-2017(R2024) A662 Grade C
0.20.15-0.51-1.60.0250.025-------
 -
5 ASME SA-841/SA-841M-2023 SA841 Grade A Class 1
0.20.15-0.51-1.60.030.030.250.250.080.35≤0.02-0.06
 -
6 ASME SA-841/SA-841M-2023 SA841 Grade B Class 1
0.150.15-0.51-1.60.030.0250.250.60.30.35≤0.02-0.06
 -
7 ASME SA-841/SA-841M-2023 SA841 Grade C Class 1
0.10.15-0.51-1.60.030.0150.250.250.080.35-0.006-0.020.06
 -
8 ASTM A841/A841M-2017 A841 Grade A Class 1
0.20.15-0.51-1.60.030.030.250.250.080.35≤0.02-0.06
 -
9 ASTM A841/A841M-2017 A841 Grade B Class 1
0.150.15-0.51-1.60.030.0250.250.60.30.35≤0.02-0.06
 -
10 ASTM A841/A841M-2017 A841 Grade C Class 1
0.10.15-0.51-1.60.030.0150.250.250.080.35-0.006-0.020.06
 -
11 EN 10028-3-2017 P355NL1, 1.0566
0.180.51.1-1.70.0250.0080.30.50.080.3≤0.020.030.1
 -
12 EN 10028-3-2017 P355NL2, 1.1106
0.180.51.1-1.70.020.0050.30.50.080.3≤0.020.030.1
 -
13 JIS G 3126-2021 SLA365
0.180.550.8-1.60.0150.01-------
 -
A841 Grade B Class 1 对应标准的历史替代
ASTM A841/A841M - 2017 ASTM A841/A841M - 2017(R2025)
同名标准
A841 Grade B Class 1 对应不同标准
1 ASTM A841/A841M-2017 通过热机械控制工艺生产的压力容器用钢板
A841 Grade B Class 1
2 ASTM A841/A841M-2017(R2025) 通过热机械控制工艺生产的压力容器用钢板
A841 Grade B Class 1
注：数据仅供参考！如有疑问，请填写"我要纠错"！
版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。
摘要 / Summary
A841 Grade B Class 1 材料牌号数据，对应标准：ASTM A841/A841M-2017，主要化学成分：C ≤0.15%，C ≤0.15%，Si 0.15–0.5%，Si 0.15–0.5%，Mn 0.7–1.35%，Mn 1–1.6%，P ≤0.03%，P ≤0.03%，材数库提供该材料的基本信息、化学成分、性能数据、相关标准及认证供应商参考信息，本页面展示的供应商为材数库认证供应商，企业资料由企业提交并经材数库审核后发布。数据来源：材数库 Caishuku.com。
推荐引用：材数库 Caishuku Material Database， 《A841 Grade B Class 1 材料牌号数据》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxOTIzMA==