基本信息
牌号 A572 Grade 55
其他名称
对应标准 ASTM A572/A572M-2018
高强度低合金钴钒结构钢技术规范
Standard Specification for High-Strength Low-Alloy Columbium-Vanadium Structural Steel
归类 合金钢
性能 高强度
化学成分
A572 Grade 55 化学元素成分含量(%)
  成分 C ③ Si ① Mn ② ③ P ④ S ④ Cu Nb ⑤ 更多
Type 1 最小值 - 0.15 - - - - 0.005 /
最大值 0.25 0.4 1.35 0.03 0.03 0.2 0.05
  成分 C ③ Si ① Mn ② ③ P S Cu V ⑥ 更多
Type 2 最小值 - 0.15 - - - - 0.01 /
最大值 0.25 0.4 1.35 0.03 0.03 0.2 0.15
  成分 C ③ Si ① Mn ② ③ P S Cu V ⑥ Nb ⑤ 更多
Type 3 最小值 - 0.15 - - - - 0.01 0.005 V+Nb：0.02~0.15⑦
最大值 0.25 0.4 1.35 0.03 0.03 0.2 0.15 0.05
  成分 C ③ Si ① Mn ② ③ P S Cu N Ti V 更多
Type 5 最小值 - 0.15 - - - - 0.003 0.006 - /
最大值 0.25 0.4 1.35 0.03 0.03 0.2 0.015 0.04 0.06
① Plates to 1-1/2 in. [40 mm] Thick, Shapes with Flange or Leg Thickness to 3 in. [75 mm] inclusive, Sheet Piling, Bars, Zees, and Rolled Tees: Si≤0.40% .
Plates Over 1-1/2 in. [40 mm] Thick and Shapes with Flange Thickness Over 3 in. [75 mm]：Si 0.15~0.40%.
② Manganese, minimum, by heat analysis of 0.80 % (0.75 % by product analysis) shall be required for all plates over 3/8 in. [10 mm] in thickness; a minimum of 0.50 % (0.45 % by product analysis) shall be required for plates 3/8 in. [10 mm] and less in thickness, and for all other products. The manganese to carbon ratio shall not be less than 2 to 1.
③ For each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximum is permitted. up to a maximum of 1.60 %.
④ maximum phosphorus content of 0.04 % and a maximum sulfur content of 0.05 % are permitted for the following materials： Structural shapes， Sheet piling， Bars， Plates with widlhs up to and including 15 in. [380 mm].
⑤ Nb：Product analysis limits = 0.004~0.06 %.
⑥ V：Product analysis limits = 0.005~0.17%
⑦ Nb+V：Product analysis limits = 0.01~0.16%.
碳当量计算
机械性能
A572 Grade 55 机械性能
抗拉强度
σb
Mpa 		屈服点
σs
Mpa 		断后伸长率或延伸率
δ
%
≥485 ≥380 (in 50mm)
≥20
基本信息
接近匹配牌号 结构钢板1-2（高强度低合金）
# 标准 牌号(等级/别名/符号) 化学成分，重量%，最大值，除非另有说明
C Si Mn P S Cr Ni Mo Cu Ti V
热处理
1 GB /T 1591-2008 Q345A, L03451
0.20.51.70.0350.0350.30.50.10.30.20.15
 -
2 GB /T 1591-2008 Q345B, L03452
0.20.51.70.0350.0350.30.50.10.30.20.15
 -
3 GB /T 1591-2008 Q345C, L03453
0.20.51.70.030.030.30.50.10.30.20.15
 -
4 GB /T 1591-2008 Q345D, L03454
0.180.51.70.030.0250.30.50.10.30.20.15
 -
5 GB /T 1591-2008 Q345E, L03455
0.180.51.70.0250.020.30.50.10.30.20.15
 -
6 ASTM A242/A242M-2013 A242 Type 1
0.15-10.150.05---≤0.2--
 -
7 CSA G40.21-2013 350WT
0.220.15-0.40.5-1.50.030.04------
 -
8 CSA G40.21-2013 380W
0.230.40.5-1.50.040.05------
 -
9 ASME SA-1011/SA-1011M-2023 HSLAS Grade 55 [380] Class 1
0.25-1.350.040.040.150.20.060.2≤0.005≤0.005
 -
10 ASME SA-1011/SA-1011M-2023 HSLAS Grade 60 [410] Class 2
0.15-1.50.040.040.150.20.060.2≤0.005≤0.005
 -
11 ASTM A1011/A1011M-2018(a) HSLAS Grade 55 [380] Class 1
0.25-1.350.040.040.150.20.060.2≤0.005≤0.005
 -
12 ASTM A1011/A1011M-2018(a) HSLAS Grade 60 [410] Class 2
0.15-1.50.040.040.150.20.060.2≤0.005≤0.005
 -
13 ASTM A588/588M-2019 A588 Grade A
0.190.3-0.650.8-1.250.030.030.4-0.650.4-0.25-0.4-0.02-0.1
 -
14 ASTM A588/588M-2019 A588 Grade B
0.20.15-0.50.75-1.350.030.030.4-0.70.5-0.2-0.4-0.01-0.1
 -
15 ASTM A588/588M-2019 A588 Grade K
0.170.25-0.50.5-1.20.030.030.4-0.70.40.10.3-0.5--
 -
16 ASTM A633/633M-2018 A633 Grade C
0.20.15-0.51.15-1.50.030.03------
 -
17 ASTM A633/633M-2018 A633 Grade D
0.20.15-0.50.7-1.350.030.030.250.250.080.35--
 -
18 ASME SA-572/SA-572M-2023 SA572 Grade 55[380] Type1
0.250.15-0.41.350.030.03---0.2--
 -
19 ASME SA-572/SA-572M-2023 SA572 Grade 55[380] Type2
0.250.15-0.41.350.030.03---0.2-0.01-0.15
 -
20 ASME SA-572/SA-572M-2023 SA572 Grade 55[380] Type3
0.250.15-0.41.350.030.03---0.2-0.01-0.15
 -
21 ASME SA-572/SA-572M-2023 SA572 Grade 55[380] Type5
0.250.15-0.41.350.030.03---0.20.006-0.040.06
 -
22 ASTM A572/A572M-2018 A572 Grade 55, Gr55
0.250.15-0.41.350.030.03---0.20.006-0.040.06
 -
23 ASTM A656/A656-2024 A656 Grade 60[415] Type 3
0.180.61.650.0250.03-----0.08
 -
24 ASTM A656/A656-2024 A656 Grade 60[415] Type 7
0.180.61.650.0250.03-----0.15
 -
25 ASTM A656/A656-2024 A656 Grade 60[415] Type 8
0.180.61.650.0250.03----0.150.15
 -
供应信息

材料牌号对应供应商

告诉我在“材数库”看到，将给您优惠

1
福临(天津)国际贸易有限公司
主营: 国内各大钢厂材质系列钢材品种 出包打包 精包装 截尺 切割 加工钢结构 喷漆 镀锌 仓储 激光 涂油 打孔 冲压 抛丸除锈 焊接 折弯 开平纵剪 压槽套丝 圆改方 油纸包装 框架包装 集装箱掏箱 集装箱装箱
  • 联系人：林辉
  • 手机： 18902023629
  • 电话：18902023629
  • 微信：13821453838
棒材：5.0-350mm冷拉：热轧；板材：1.0-80mm热轧、型钢5#-45#热轧、管材20mm-600mm热轧。
询价
注：数据仅供参考！如有疑问，请填写"我要纠错"！
版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。
摘要 / Summary
A572 Grade 55 材料牌号数据，其他名称/统一牌号：Gr55，对应标准：ASTM A572/A572M-2018，主要化学成分：C ≤0.25%，C ≤0.25%，C ≤0.25%，C ≤0.25%，Si 0.15–0.4%，Si 0.15–0.4%，Si 0.15–0.4%，Si 0.15–0.4%，Mn ≤1.35%，Mn ≤1.35%，Mn ≤1.35%，Mn ≤1.35%，P ≤0.03%，P ≤0.03%，P ≤0.03%，P ≤0.03%，S ≤0.03%，S ≤0.03%，S ≤0.03%，S ≤0.03%，Cu ≤0.2%，Cu ≤0.2%，Cu ≤0.2%，Cu ≤0.2%，N 0.003–0.015%，Ti 0.006–0.04%，V 0.01–0.15%，V 0.01–0.15%，V ≤0.06%，Nb 0.005–0.05%，Nb 0.005–0.05%，/#$#/#$#V+Nb：0.02~0.15⑦#$#/。数据来源：材数库 Caishuku.com。
推荐引用：材数库 Caishuku Material Database， 《A572 Grade 55 材料牌号数据》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxOTE4NA==