F594 416Se S41623 - ASTM F594-2009(2015)

牌号	F594 416Se
美国UNS	S41623
对应标准	ASTM F594-2009(R2015) 不锈钢螺母标准规范 Standard Specification for Stainless Steel Nuts
归类	马氏体不锈钢

F594 416Se 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Se
最小值	-	-	-	-	-	12	0.15
最大值	0.15	1	1.25	0.06	0.06	14	-

碳当量计算

F594 416Se 机械性能

公称直径 inch	热处理或状态	硬度 HBW
1/4 ~ 1-1/2	H	HR（C20~30）
1/4 ~ 1-1/2	HT	HR（C34~45）

注：
A——Machined from annealed or solution annealed stock thus retaining the properties of the original material, or hot formed and solution annealed.
AF——Annealed after all threading is completed.
AH——Solution annealed and age hardened after forming.
CW——Annealed and cold worked Sizes 0.75 in. and larger may be hot worked and solution annealed.
H——Hardened and tempered at 1050°F (566℃) min.
HT——Hardened and tempered at 525°F (274℃) min.
SH——Machined from strain hardened stock.

注：数据仅供参考！如有疑问，请填写"我要纠错"！