F593 416Se S41623 - ASTM F593-2017

牌号	F593 416Se
美国UNS	S41623
对应标准	ASTM F593-2017 不锈钢螺栓、六角螺钉和螺柱标准规范 Standard Specification for Stainless Steel Bolts, Hex Cap Screws, and Studs
归类	马氏体不锈钢

F593 416Se 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Se
最小值	-	-	-	-	-	12	0.15
最大值	0.15	1	1.25	0.06	0.06	14	-

碳当量计算

F593 416Se 机械性能

	热处理或状态	抗拉强度 σ_b ksi	屈服点 σ_s ksi	断后伸长率或延伸率 δ %	硬度 HBW
1/4 ~ 1-1/2 (全尺寸)	H	110~140	≥90		HR (C20~30)
1/4 ~ 1-1/2 (全尺寸)	HT	160~190	≥120		HR (C34~45)
1/4 ~ 1-1/2 (机加工)	H	≥110	≥90	≥18
1/4 ~ 1-1/2 (机加工)	HT	≥160	≥120	≥12

注1： “全尺寸”指的拉力测试试件是使用前的状态未经改变的完整的紧固件产品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.