牌号	GX40NiCrSi35-25
德国W-Nr.	1.4857
对应标准	DIN 17465-1993 耐热铸钢 Heat Resisting Steel Castings - Technical Delivery Conditions
归类	铸钢
标签	奥氏体型耐热铸钢最高工作温度1100°C

GX40NiCrSi35-25 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	0.3	1	-	-	-	24	34
最大值	0.5	2.5	1.5	0.035	0.03	26	36

碳当量计算

GX40NiCrSi35-25 机械性能

产品	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
铸钢	铸态	≥440①	≥230	≥5①	-

①适用于厚度t≤25mm的产品

高温性能及最高使用温度

Material 1% creep limit after 10000 h, in N/mm²,
at a temperature, in °C, of Maximum service
temperature,
in °C
designation number 600 700 800 900 1000 1100
GX40NiCrSi35-25 1.4857 - 70 40 20 8 2 1100

物理性能

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
GX40NiCrSi35-25	1.4857	8	14.6	0.50	15.5	17.0	18.0

焊接资料

Material suitable fillet metal Heat treatment
designation number Covered
electrode
(symbol) Wire or rod
(symbol) Material number prior to welding after welding
GX40NiCrSi35-25 1.4857 25 35Nb X40NiCrNb35-25 1.4853 - -

1 近似对照表耐热铸钢和耐热合金铸件

中国		中国台湾	日本	韩国	美国		国际标准组织	德国		法国	英国
GB	ISC	CNS	JIS	KS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG40Ni35Cr26Si2	C53941	SCH 24	SCH 24X	HRSC 24	HP	J95705	GX40NiCrSi35-26	GX40NiCrSi35-25	1.4857	GX40NiCrSi35-26	GX40NiCrSi35-26

2 近似对照表耐蚀铸钢（不锈钢铸件）

中国	美国	德国
GB	ASTM	DIN EN/DIN	W-Nr.
ZG4Cr25Ni35Si2	HP	G-X45NiCrSi35 25	1.4857

3 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.
ZG4Cr25Ni35Si2	SCH24	HP	J95705	G-X45CrNiSi35 25	1.4857

注：数据仅供参考！如有疑问，请填写"我要纠错"！