牌号	GX40CrNiSi27-4
德国W-Nr.	1.4823
对应标准	DIN 17465-1993 耐热铸钢 Heat resisting steel castings - Technical delivery conditions
归类	铸钢
标签	铁素体-奥氏体耐热铸钢最高工作温度1100°C

GX40CrNiSi27-4 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	0.35	1	-	-	-	25	3.5
最大值	0.5	2.5	1.5	0.035	0.03	28	5.5

碳当量计算

GX40CrNiSi27-4 机械性能

产品	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
铸钢	铸态	-	-	-	-

高温性能及最高使用温度

Material 1% creep limit after 10000 h, in N/mm²,
at a temperature, in °C, of Maximum service
temperature,
in °C
designation number 600 700 800 900 1000 1100
GX40CrNiSi27-4 1.4823 - 21 9 4 1.5 - 1100

物理性能

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
GX40CrNiSi27-4	1.4823	7.6	16.7	0.50	13.0	14.5	16.5

焊接资料

Material		suitable fillet metal			Heat treatment
designation	number	Covered electrode (symbol)	Wire or rod (symbol)	Material number	prior to welding	after welding
GX40CrNiSi27-4	1.4823	25 4 25 20 29 9	X12CrNi25-4 X12CrNi25-20 X10CrNi30-9	1.4820 1.4842 1.4337	大截面或横截面不同的产品需预热	不需热处理

1 近似对照表耐热铸钢和耐热合金铸件

中国		中国台湾	日本	韩国	美国		国际标准组织	德国		法国	英国
GB	ISC	CNS	JIS	KS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG40Cr27Ni4Si2	C54890	SCH 11	SCH 11X	HRSC 11	HD	J93005	GX40CrNiSi27-4	GX40CrNiSi27-4	1.4823	Z30CN26.05M	GX40CrNiSi27

2 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	BS EN/BS
ZG5Cr25Ni2	SCH2	HC	J92605	G-X40CrNi24 5	1.4822 1.4823	452C11

GX40CrNiSi27-4 对应不同标准

1	EN 10295-2002 耐热钢铸件
	GX40CrNiSi27-4 1.4823
2	DIN 17465-1993 耐热铸钢
	GX40CrNiSi27-4 1.4823

注：数据仅供参考！如有疑问，请填写"我要纠错"！