基本信息
| 牌号 | NiCr20TiAI |
|---|---|
| 2.4952 | |
| 对应标准 | NF EN 10090-1998
阀门用钢和合金 Valve Steels and Alloys for Internal Combustion Engines |
| 归类 | 镍及镍合金 |
| 密度 | 8.3 g/cm3 |
化学成分
机械性能
-
高温抗拉强度
Designation Reference heat
treatment
conditionTensile strength at:
N/mm2 ①Name Number 500°C 550°C 600°C 650°C 700°C 750°C 800°C NiCr20TiAI 2.4952 +AT+P 1050 1030 1000 930 820 680 500 ① The values given here are situated near the lower limit of the scatter range. -
高温屈服强度
Designation Reference heat
treatment
condition0.2% proof strength at:
N/mm2 ①Name Number 500°C 550°C 600°C 650°C 700°C 750°C 800°C NiCr20TiAI 2.4952 +AT+P 700 650 650 600 600 500 450 ① The values given here are situated near the lower limit of the scatter range. -
蠕变强度
Designation Creep strength after 1000 h at:
N/mm2 ①Name Number 500°C 650°C 725°C 800°C NiCr20TiAI 2.4952 - 500 290 150 ① Mean values of scatter range determined until now. -
热处理指南
Designation Hot forming
℃Soft
annealing
℃Quenching or
solution heat
treatment
℃Quenching
agentTempering or
artificial ageing
℃Name Number NiCr20TiAI 2.4952 1150 to 1050 - 1000 to 1080 a or w 690 to 710/
16h a◎ a=air; o=oil; w=water -
物理性能
静态弹性模量 20°C与各温度间热膨胀系数 热导率 比热容 磁性 20°C 100°C 300°C 500°C 700°C 20°C 20°C 无 KN/mm2 10-6 K-1 W/m.K J/kg.K 215 11.9 13.1 13.7 14.5 13 460
NiCr20TiAI 对应标准的历史替代
同名标准
统一牌号
注：数据仅供参考！如有疑问，请填写"我要纠错"！
摘要 / Summary
NiCr20TiAI 材料牌号数据，对应标准：NF EN 10090-1998，主要化学成分：Fe ≤3%，C 0.04–0.1%，Si ≤1%，Mn ≤1%，P ≤0.02%，S ≤0.015%，Cr 18–21%，Ni ≥65%，密度约 8.3 g/cm³，材数库提供该材料的基本信息、化学成分、性能数据、相关标准及认证供应商参考信息，本页面展示的供应商为材数库认证供应商，企业资料由企业提交并经材数库审核后发布。数据来源：材数库 Caishuku.com。
推荐引用：材数库 Caishuku Material Database，
《NiCr20TiAI 材料牌号数据》，
https://www.caishuku.com/material/detail.php?mid=azhlNWIxMjEzODU=