S275ML 1.8819 - EN 10025-4-2004

牌号	S275ML
欧标钢号	1.8819
对应标准	EN 10025-4-2004 结构钢热轧产品第4部分热机械轧制可焊接细晶粒结构钢

S275ML 化学元素成分含量(%)

成分	C ^*	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu ^④	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	-	-	-	-	-	-	-	-	-	-	-	0.015
最大值	0.15	0.55	1.6	0.03	0.025	0.35	0.35	0.6	0.13	0.017	0.06	0.1	0.06	-

① For long products the P and S content can be 0.005% higher.
② For railway applications a maximum S content of 0.012% may be agreed at the time of enquiry and order.
③ If sufficient other N-binding elements are present the minimum total AI content does not apply.
④ Cu content above 0.45% may cause hot shortness during hot forming.

* For long products a maximum C content of 0.17% for grade S275 and a maximum C content of 0.18% for grade S355 applies.