X2CrNiN18-7 1.4318 - NF EN 10088-2-2005

牌号	X2CrNiN18-7
	1.4318
对应标准	NF EN 10088-2-2005 普通用途不锈钢板和钢带的交货技术条件 Part2:Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
归类	奥氏体不锈钢
标签	标准等级

X2CrNiN18-7 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	N
最小值	-	-	-	-	-	16.5	6	0.1
最大值	0.03	1	2	0.045	0.015	18.5	8	0.2

◎ 未经买方同意，不得随意向钢中添加表中未列的元素，冶炼精加工除外。采取一切必要措施以防在废钢和生产原料中带入这些元素，因为其会削弱钢的机械性能，降低钢的适用性。

◎ 在询价和订购时可商定更严格的碳含量范围。

碳当量计算

X2CrNiN18-7 机械性能

条件	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
冷轧带钢：T ≤ 8mm	+AT	650~850	( t ) Rp0.2：≥ 350①③ Rp1.0：≥ 380①② ③	( t ) T＜3mm：≥35③④ T ≥ 3mm：≥40③⑤	-
热轧带钢：T ≤ 13.5mm	+AT	650~850	( t ) Rp0.2：≥ 330①③ Rp1.0：≥ 370①② ③	( t ) T＜3mm：≥35③④ T ≥ 3mm：≥40③⑤	（T＞10mm） I：≥ 90；t：≥60
热轧中厚板：T ≤ 75mm⑥	+AT	630~830	( t ) Rp0.2：≥ 330①③ Rp1.0：≥ 370①② ③	( t ) T＜3mm：≥45③④ T ≥ 3mm：≥45③⑤	（T＞10mm） I：≥ 90；t：≥60
钢材（工艺流程2H）：	冷加工+C850⑦⑧	850~1000
钢材（工艺流程2H）：	冷加工+C1000⑦⑧	1000~1150
钢材（工艺流程2H）：	冷加工+CP500⑦⑧		500~700
钢材（工艺流程2H）：	冷加工+CP700⑦⑧		700~900

◎ T-厚度；l-纵向; t-横向
◎ +A=软化退火；+QT=淬火及回火；+P=沉淀硬化；+AT=固溶退火；+SR=消除应力

① 对于连续热轧产品，可在询价和订购时商定Rp0.2(即表中σs)的最小值提高20MPa，Rp1.0的最小值提高10MPa。
② 仅作指导
③ 如果在轧制宽度<300mm的情况下，采用纵向试验件，最小值减小如下:屈服强度-15MPa，恒定标距的延伸率-5%，比例标距延伸率-2%。
④ T＜3mm时适用于标距为80mm、宽度为20mm的试件。也可以使用标距为50mm、宽度为12.5mm的试件。
⑤ T ≥3mm时适用于标距为5.65√S的试件。
⑥ T＞75mm，可以协商机械性能。
⑦ 可商定中间抗拉强度和屈服强度值。另外可以指定钢最小0.2%-耐强度或硬度，但订单中只能指定一个参数。
⑧ 每个抗拉强度和屈服强度等级的最大产品厚度随着抗拉强度的增大而减小。最大产品厚度和剩余延伸率也取决于钢的加工硬化行为和冷加工条件。因此，可能要求制造商提供更准确的信息。
* 交货条件下有抗晶间腐蚀; 致敏条件下有抗晶间腐蚀（根据EN ISO 3651-2进行测试）。

交付条件下在高温下的最小屈服强度

Material designation		Heat treatment condition	Minimum 0.2%-proof strength,MPa at a temperature (in°C) of:										Minimum 1%-proof strength,MPa at a temperature (in°C) of:
Name	Number	Heat treatment condition	100	150	200	250	300	350	400	450	500	550	100	150	200	250	300	350	400	450	500	550
X2CrNiN18-7	1.4318	+AT	265	200	185	180	170	165	-	-	-	-	300	235	215	210	200	195	-	-	-	-

符合本欧洲标准的产品热处理指南

Material designation		Hot forming		Heat treatment symbol	Solution anneailing
Name	Number	Temperature ℃	Type of cooling	Heat treatment symbol	Temperature①②③ ℃	Type of cooling④
X2CrNiN18-7	1.4318	1150 to 850	air	+AT	1020 to 1100	water,air

◎ Temperature of solution annealing shall be agreed for simulated heat-treated test pieces.
① Solution annealing may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained.
② If heat treatment is carried out in a continuous furnace, the upper part of the range specified is usually preferred, or even exceeded.
③ Lower end of the range specified for solution annealing should be aimed at the heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing, a temperature of 980℃ is adequate as a lower limit for Mo-free steels, a temperature of 1000℃ for steels with Mocontents up to 3 % and a temperature of 1020°C for steels with Mo contents exceeding 3 %.
④ Cooling sufficiently rapidly in order to avoid the occurrence of intergranular corrosion as defined in EN ISO 3651-2.

X2CrNiN18-7 对应不同标准

1	EN 10088-1-2005 不锈钢第1部分:不锈钢的清单
	X2CrNiN 18-7 1.4318
2	EN 10296-2-2005 机械工程和一般工程用焊接圆钢管.交货技术条件.第2部分:不锈钢
	X2CrNiN18-7 1.4318
3	ISO TS 15510-2003 技术规范不锈钢-化学成分
	X2CrNiN18-7
4	ISO 15510-2014 技术规范不锈钢-化学成分
	X2CrNiN18-7 4318-301-53-I
5	ISO 9328-7-2018 不锈钢承压扁钢制品
	X2CrNiN18-7
6	NF EN 10088-2-2005 普通用途不锈钢板和钢带的交货技术条件
	X2CrNiN18-7 1.4318
7	NF EN 10088-1-2005 不锈钢 - 第1部分：不锈钢清单
	X2CrNiN18-7 1.4318
8	NF EN 10028-7-2008 压力容器用不锈钢扁平产品
	X2CrNiN18-7 1.4318
9	NF EN 10296-2-2005 机械和一般工程用焊接圆钢管-交货技术条件-第2部分:不锈钢管
	X2CrNiN18-7 1.4318
10	NF EN 10028-7-2000 压力容器用不锈钢扁平产品
	X2CrNiN18-7 1.4318

注：数据仅供参考！如有疑问，请填写"我要纠错"！