Name: A569 Type A Material Data
Creator: 材数库 Caishuku
License: https://www.caishuku.com/ai-license.html

材数库 Caishuku

基本信息

牌号	A569 Type A
对应标准	ASTM A569/A569M-1998 钢，碳(含量最大0.15%)，商用热轧薄板和带材 Standard Specification for Steel, Carbon (0.15 Maximum, Percent), Hot-Rolled Sheet and Strip Commercial
归类	碳钢
标签	薄板带材

化学成分

A569 Type A 化学元素成分含量(%)

成分	C	Mn	P	S	Cr	Ni	Cu	Mo	Ti	V	Nb
最小值	-	-	-	-	-	-	-	-	-	-	-
最大值	0.1	0.6	0.03	0.035	0.15	0.2	0.2	0.06	0.008	0.008	0.008

①Types A and C may be furnished as vacuum degassed and/or chemically stabilized at the producers option.
② For carbon levels less than or equal to 0.02%, columbium and/or titanium may be used as chemical stabilizing elements in Type A and C at the producers option. In such case, the Table limitations on such elements do not apply. Rather, the limit on columbium shall be 0.1% maximum and the limit on titanium shall be 0.15% maximum.
③Types B describes the most common product previously included in Specification A569/A569M.
④Specify Type B to avoid carbon levels below 0.02%.
⑤When an aluminum deoxidized steel is required for the application. Commercial Steel (CS) may be ordered to a minimum of 0.01% total aluminum.
⑥Where an ellipsis (...) appears in this table, there is no requirement, but the analysis shall be reported.
⑦ When copper steel is not specified, the sum of copper, nickel, chromium, and molybdenum shall not exceed 0.5% on heat analysis. When one or more of these elements is specified, the sum does not apply; in which case, only the individual limits on the remaiming elements will apply.
⑧ Chromium is permitted ,at the producers option, to 0.25% maximum when the carbon is less than or equal to 0.05%. In such case, the limit on the sum of the four elements in Footnote ⑦ does not apply.

碳当量计算

机械性能

A569 Type A 机械性能

条件	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
薄板，带材	205~345	≥25

The yield strength tends to increase and elongation tends to decrease as the sheet thickness decreases. These properties represent those typical of material in the thickness range of 0.100 to 0.150 in. (2.5 to 3.5 mm)

注：数据仅供参考！如有疑问，请填写"我要纠错"！

版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。

摘要 / Summary

A569 Type A 材料牌号数据，对应标准：ASTM A569/A569M-1998，主要化学成分：C ≤0.1%，Mn ≤0.6%，P ≤0.03%，S ≤0.035%，Cr ≤0.15%，Ni ≤0.2%，Cu ≤0.2%，Mo ≤0.06%，材数库提供该材料的基本信息、化学成分、性能数据、相关标准及认证供应商参考信息，本页面展示的供应商为材数库认证供应商，企业资料由企业提交并经材数库审核后发布。数据来源：材数库 Caishuku.com。

推荐引用：材数库 Caishuku Material Database，《A569 Type A 材料牌号数据》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxMTgxODE=

A569 Type A 的供应商信息由材数库认证企业提供。本页面展示的企业均为材数库认证供应商，企业名称、联系人、联系方式、主营产品及供货信息由企业提交，经材数库审核后发布并持续维护。