基本信息
牌号 ENiCrFeCo
W83002
对应标准 AWS A5.13/A5.13M-2010
堆焊焊条规范 保护金属电弧焊
Specification for Surfacing Electrodes for Shielded Metal Arc Welding
标签 镍基堆焊焊条
说明 Characteristics. Weld metal deposited by these electrodes contain a fairly large volume fraction of hypereutectic chromium carbides distributed throughout the microstructure. The alloy offers many of the same high-performance characteristics of deposits made using ECoCr-C or ENiCr-C electrodes in terms of abrasive wear resistance. The reduced nickel or cobalt content, or both, lowers corrosion properties and galling resistance. The high volume fraction of carbides makes this alloy sensitive to cracking during cooling.
Applications. Welds made using ENiCrFeCo electrodes are preferred where high abrasion (low impact) is a major factor. Typical applications are feed screws, slurry pumps, and mixer components.
类别 合金钢
化学成分
ENiCrFeCo 化学元素成分含量(%)
成分 Fe C Si Mn P S Cr Ni Mo W Co 其他合计
最小值 20 2.2 0.6 - - - 20 10 7 2 10 -
最大值 25 3 1.5 1 0.03 0.03 30 33 10 4 15 1
其他单个或其他合计化学成分包括表中未指定值的化学成分。只有在假定存在或在常规分析中，且有迹象表明其成分将超过规定值的情况下，才应进行分析。
注：数据仅供参考！如有疑问，请填写"我要纠错"！
版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。
摘要 / Summary
ENiCrFeCo 材料牌号数据，对应标准：AWS A5.13/A5.13M-2010，主要化学成分：Fe 20–25%，C 2.2–3%，Si 0.6–1.5%，Mn ≤1%，P ≤0.03%，S ≤0.03%，Cr 20–30%，Ni 10–33%，Characteristics. Weld metal deposited by these electrodes contain a fairly large volume fraction of hypereutectic chromium carbides distributed throughout the microstructure。
推荐引用：材数库 Caishuku Material Database， 《ENiCrFeCo 材料牌号数据》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxMTUzNDA=
ENiCrFeCo 的供应商信息由材数库认证企业提供。 本页面展示的企业均为材数库认证供应商， 企业名称、联系人、联系方式、 主营产品及供货信息由企业提交， 经材数库审核后发布并持续维护。
对比 0