S420ML 1.8836 - EN 10025-4-2019

牌号	S420ML
欧标钢号	1.8836
对应标准	EN 10025-4-2019 热机械轧制可焊接细晶粒结构钢 Technical delivery conditions for thermomechanical rolled weldable fine grain structural steels
归类	合金钢

S420ML 化学元素成分含量(%)

成分	C ^④	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	-	-	-	-	-	-	-	-	-	-	-	0.02
最大值	0.16	0.5	1.7	0.025	0.02	0.3	0.8	0.55	0.2	0.025	0.05	0.12	0.05	-

① For long products the P and S content can be 0.005% higher.
② For some applications, e.g. for railways, a maximum S content of 0,010 % may be agreed upon at the time of the order.
③ If sufficient other N-binding elements are present the minimum total Al content does not apply.
④ For long products of the grades S420 a maximum C content of 0,18 % applies.

碳当量计算

S420ML 机械性能

厚度 t mm	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
t≤16	520~680	≥420	≥19
16＜t≤40	520~680	≥400	≥19
40＜t≤63	500~660	≥390	≥19
63＜t≤80	480~640	≥380	≥19
80＜t≤100	470~630	≥370	≥19
100＜t≤150	460~620	≥365	≥19

近似对照表结构、压力容器和工程钢

美国	德国	法国	欧标
ASTM	DIN EN/DIN	NF EN/NF	EN	数字牌号
A633Gr.E	TStE420TM	E420FP	S420ML FeE420KTTM①	1.8836

S420ML 对应不同标准

1	EN 10025-4-2004 结构钢热轧产品第4部分热机械轧制可焊接细晶粒结构钢
	S420ML 1.8836
2	EN 10025-4-2019 热机械轧制可焊接细晶粒结构钢
	S420ML 1.8836

注：数据仅供参考！如有疑问，请填写"我要纠错"！