C50 - ISO 683-18-2014

牌号	C50
对应标准	ISO 683-18-2014 热处理钢、合金钢和易切削钢 -- 第18部分：光面钢制品 Bright steel products
归类	碳钢

C50 化学元素成分含量(%)

成分	C	Si ^①	Mn	P	S	Cr	Ni	Cu	Mo	更多
最小值	0.47	0.1	0.6	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
最大值	0.55	0.4	0.9	0.045	0.045	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

① Steels may be supplied with a lower silicon content. In this case, alternative means of deoxidation shall be used.
② Steels with improved machinability either by higher sulfur levels up to about 0,10 % S (including controlled sulphide morphology) or lead additions may be available on request. In the first case, the upper limit of the Mn-content may be increased by 0,15 %.

碳当量计算

C50 机械性能

厚度 t mm	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	770~1100	≥590	≥5
10＜t≤16	Cold drawn (+C)	730~1080	≥520	≥6
16＜t≤40	Cold drawn (+C)	690~1050	≥440	≥7
40＜t≤63	Cold drawn (+C)	650~1030	≥390	≥8
16＜t≤100	As-rolled + peeled (+SH)	610~910			179~269

注：Steels C50 in delivery condition +C may be soft annealed before cold drawing.

1 近似对照表碳素结构钢和工程用钢

中国	日本	国际标准组织
GB	JIS	ISO
50	S50C	C50

2 近似对照表优质碳素结构钢

中国	日本	美国	国际标准组织	德国	法国	欧标		俄罗斯	瑞典	英国
GB	JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	数字牌号	GOST	SS	BS EN/BS
50	S50C	1049 1050	C50 C50E4	C50 Ck50	XC48H1	C50	1.0540	50	1674	070M50 080M50

3 近似对照表优质碳素结构钢

中国	日本	美国	国际标准组织	法国	俄罗斯	英国
GB	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
GB/T 699-1999 50	S50C	1049 1050	ISO 630-1:1987 C50 C50E4 C50M2	C50 XC48	50	060A52

C50 对应不同标准

1	ISO 683-18-1996 热处理钢、合金钢和易切削钢
	C50
2	DIN 17200-1987 调质钢材的供货技术条件
	C50 1.0540
3	EN 10250-2-2000 一般工程用自由锻钢锻件.第2部分:非合金钢和特种钢
	C50 1.0540
4	ISO 683-1-2016 淬火和回火用非合金钢
	C50
5	DIN EN ISO 683-1-2018 热处理钢、合金钢和易切削钢 -- 第1部分：调质非合金钢
	C50
6	ISO 683-18-2014 热处理钢、合金钢和易切削钢 -- 第18部分：光面钢制品
	C50
7	NF A 37-502-1984 结构钢冷轧钢带
	C50

注：数据仅供参考！如有疑问，请填写"我要纠错"！