C30 - ISO 683-18-2014

牌号	C30
对应标准	ISO 683-18-2014 热处理钢、合金钢和易切削钢 -- 第18部分：光面钢制品 Bright steel products
归类	碳钢

C30 化学元素成分含量(%)

成分	C	Si ^①	Mn	P	S	Cr	Ni	Cu	Mo	更多
最小值	0.27	0.1	0.5	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
最大值	0.34	0.4	0.8	0.045	0.045	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

① Steels may be supplied with a lower silicon content. In this case, alternative means of deoxidation shall be used.
② Steels with improved machinability either by higher sulfur levels up to about 0,10 % S (including controlled sulphide morphology) or lead additions may be available on request. In the first case, the upper limit of the Mn-content may be increased by 0,15 %.

碳当量计算

C30 机械性能

厚度 t mm	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	610~910	≥455	≥6
10＜t≤16	Cold drawn (+C)	570~870	≥420	≥7
16＜t≤40	Cold drawn (+C)	550~850	≥345	≥8
40＜t≤63	Cold drawn (+C)	520~820	≥300	≥9
63＜t≤100	Cold drawn (+C)	480~780	≥250	≥9
16＜t≤100	As-rolled + peeled (+SH)	480~680			143~198

1 近似对照表碳素结构钢和工程用钢

中国	日本	国际标准组织
GB	JIS	ISO
30	S30C	C30

2 近似对照表优质碳素结构钢

中国	日本	美国	国际标准组织	德国		法国	欧标		俄罗斯	英国
GB	JIS	SAE	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	数字牌号	GOST	BS EN/BS
30	S30C	1030	C30 C30E4	C30 Ck30	1.0528	AF50C30 XC32	C30	1.0528	30	080M32 En5

3 近似对照表优质碳素结构钢

中国	日本	美国	国际标准组织	法国	俄罗斯	英国
GB	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
GB/T 699-1999 30	S30C	1030	ISO 630-1:1987 C30 C30E4 C30M2	C30 XC32	30	060A30

C30 对应不同标准

1	ISO 683-18-1996 热处理钢、合金钢和易切削钢
	C30
2	DIN 17200-1987 调质钢材的供货技术条件
	C30 1.0528
3	JIS G 7401-2000 冷锻及冷轧挤压用钢
	(C30) 25CrMo4E
4	ISO 4954-1993 冷镦和冷挤压用钢
	(C30) 25CrMo4E
5	EN 10250-2-2000 一般工程用自由锻钢锻件.第2部分:非合金钢和特种钢
	C30 1.0528
6	ISO 683-1-2016 淬火和回火用非合金钢
	C30
7	DIN EN ISO 683-1-2018 热处理钢、合金钢和易切削钢 -- 第1部分：调质非合金钢
	C30
8	ISO 683-18-2014 热处理钢、合金钢和易切削钢 -- 第18部分：光面钢制品
	C30

注：数据仅供参考！如有疑问，请填写"我要纠错"！