S41041 - ASTM A565/A565M-2010(R2017)-材数库

基本信息

美国UNS	S41041
对应标准	ASTM A565/A565M-2010(R2017) 高温用马氏体不锈钢棒 Martensitic Stainless Steel Bars for High-Temperature Service
归类	马氏体不锈钢

化学成分

化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo	Nb	Al
最小值	0.13	-	0.4	-	-	11.5	-	-	0.15	-
最大值	0.18	0.5	0.6	0.03	0.03	13	0.5	0.2	0.45	0.05

碳当量计算

机械性能

条件	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	断面收缩率 ψ %	硬度 HBW	冲击吸收能量 KV2 J
HT - Heat treated (for high-temperature service)	≥795	≥515	≥15	≥50	≤277	≥27

① HT - Heat treated (for high-temperature service)：2075 to 2125°F [1135 to 1165°C] for 2 h min, quench in air or oil and temper at 1250°F (675°C] min for 2 h min.

统一牌号

S41041 统一牌号UNS

1	ASTM A565/A565M-2010(R2017) S41041
2	ASTM A959-2019 S41041
3	ASTM A982/A982M-2010(R2025) A982 Grade E Class 1 S41041
4	ASTM A982/A982M-2010(R2025) A982 Grade E Class 2 S41041
5	ASTM A1021/A1021M-2020(R2025) A1021 Grade E Class 1 S41041
6	ASTM A1021/A1021M-2020(R2025) A1021 Grade E Class 2 S41041
7	ASTM A1021/A1021M-2020(R2025) A1021 Grade E Class 3 S41041
8	ASTM A 1028-2003(R2015) A1028 Grade E Class 1 S41041
9	ASTM A 1028-2003(R2015) A1028 Grade E Class 2 S41041

注：数据仅供参考！如有疑问，请填写"我要纠错"！

版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。