繁體中文 | English
基本信息
牌号 EFeMnCr
W79710
对应标准 AWS A5.13/A5.13M-2010
堆焊焊条规范 保护金属电弧焊
Specification for Surfacing Electrodes for Shielded Metal Arc Welding
标签 铁基堆焊焊条
说明 Characteristics. Weld metal deposited by EFeMnCr electrodes have characteristics similar to austenitic manganese deposits. The high chromium content imparts stainless steel qualities. These deposits cannot be flame cut. Although care must be taken in application to avoid heat build-up, deposits are more stable than FeMn series electrodes.
Applications. Like EFeMn type electrodes, EFeMnCr electrodes are used for rebuilding, repair, and joining of equipment made of Hadfield austenitic manganese steel. EFeMnCr electrodes offer the added advantage of being usable for joining austenitic manganese steel both to itself and to carbon steel. EFeMnCr weld metals often are used as a base for surfacing with EFeCr types for parts subject to both wear and impact.
类别 合金钢
化学成分
EFeMnCr 化学元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo V 其他合计 更多
最小值 0.25 - 12 - - 13 0.5 - - - Fe:余量
最大值 0.75 1.3 18 0.035 0.035 17 2 2 1 1
其他单个或其他合计化学成分包括表中未指定值的化学成分。只有在假定存在或在常规分析中，且有迹象表明其成分将超过规定值的情况下，才应进行分析。
碳当量计算
注：数据仅供参考！如有疑问，请填写"我要纠错"！
版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。
摘要 / Summary
EFeMnCr 材料牌号数据，对应标准：AWS A5.13/A5.13M-2010，主要化学成分：C 0.25–0.75%，Si ≤1.3%，Mn 12–18%，P ≤0.035%，S ≤0.035%，Cr 13–17%，Ni 0.5–2%，Mo ≤2%，Characteristics. Weld metal deposited by EFeMnCr electrodes have characteristics similar to austenitic manganese deposits. The high chromium content imparts stainless steel。