01 钢铁产品处理状态符号
核心作用：标识钢铁产品的加工或热处理状态，反映产品的工艺特性。
符号规则：符号与前面的名称用 “+” 分隔。
主要符号及含义：
代号 | 含义（英） | 含义（中） |
+A | soft annealed | 软化退火 |
+AC | Annealed to achieve spheriodised carbides | 球化退火 |
+AR | as rolled (without any special rolling and/or heat treatment conditions) | 轧制（无任何特殊轧制和/或热处理条件） |
+AT | solution annealed | 固溶退火 |
+C | cold work hardened | 冷作(拉)硬化 |
+Cnnn | cold work hardened with a minimum tensile strength of nnn MPa | 冷加工硬化，最低抗拉强度为nnn MPa |
+CPnnn | cold work hardened with a minimum 0.2% proof strength of nnn MPa | 冷加工硬化，最低屈服强度为nnn Mpa |
+CR | cold rolled | 冷轧 |
+DC | delivery condition at manufacturer's discretion | 交货条件由制造商决定 |
+FP | treated to ferritic-pearlite structure and hardness range | 经过处理获得铁素体－球光体结构，且达到硬度范围 |
+HC | hot rolled followed by cold hardening | 热轧后冷硬化 |
+I | isothermically treated | 恒温退火 |
+LC | skin passed (temper rolled or cold drawn) | 平整（回火轧制或冷拔） |
+M | thermomechanically formed | 热机械成形 |
+N | normalised or normalised formed | 正火或正火成形 |
+NT | normalised and tempered | 正火和回火 |
+P | precipitation hardened | 沉淀硬化 |
+Q | quenched | 淬火 |
+QA | air quenched | 空冷淬火 |
+QO | oil quenched | 油淬 |
+QT | quenched and tempered | 淬火和回火，调质 |
+QW | water quenched | 水淬 |
+RA | recrystallisation annealed | 再结晶退火 |
+S | treated for cold shearing | 冷剪处理 |
+SR | stress relieved | 应力消除 |
+T | tempered | 回火 |
+TH | treatment to hardness range | 处理到硬度范围 |
+U | untreated | 未经处理的 |
+WW | warm worked | 热作 |
02 钢铁产品镀层及特殊要求符号
核心作用：标识钢铁产品的特殊性能要求，这些要求通常属于钢铁本身特性，因实际需要作为产品符号处理。
符号规则：符号与前面的名称用 “+” 分隔。
主要符号及含义：
代号 | 含义（英） | 含义（中） |
+CH | core hardenability | 芯部可淬性 |
+H | hardenability | 可淬透性 |
0 | through thickness property; minimum reduction of area= 15 % | 厚度方向性能级别；最小断面收缩率=15% |
0 | through thickness property; minimum reduction of area = 25 % | 厚度方向性能级别；最小断面收缩率=25% |
0 | through thickness property; minimum reduction of area = 35 % | 厚度方向性能级别；最小断面收缩率=35% |
+A | hot dip aluminium coating | 热浸铝涂层 |
+AS | aluminium silicon alloy coating | 铝硅合金涂层 |
+AZ | aluminium zinc alloy(> 50 % Al) coating | 铝锌合金（>50%铝）涂层 |
+GE | electrolytic chromium/chromium oxide coating (EGGS) | 电解铬/氧化铬涂层(EGGS) |
+CU | copper coating | 镀铜 |
+IC | inorganic coating | 无机涂料 |
+OC | organic coating | 有机涂层 |
+S | hot dip tin coating | 热浸镀锡 |
+SE | electrolytic tin coating | 电解镀锡 |
+T | hot dip lead tin alloy (terne) coating | 热浸铅锡合金镀层 |
+TE | electrolytic lead tin alloy (terne) coating | 电解铅锡合金镀层 |
+Z | hot dip zinc (galvanised) coating | 热浸锌（镀锌）涂层 |
+ZA | hot dip zinc aluminium(> 50 % Zn) coating | 热浸镀锌铝（>50%锌）涂层 |
+ZE | electrolytic zinc coating | 电解镀锌 |
+ZF | hot dip zinc iron (galvannealed) coating | 热浸镀锌铁（电镀）涂层 |
+ZN | electrolytic zinc nickel alloy coating | 电解锌镍合金镀层 |
03 钢铁产品选择示例
场景示例1 桥梁结构用高强度钢板（需厚度方向性能与抗腐蚀涂层）需求分析：桥梁承重结构需承受垂直载荷和环境腐蚀，要求钢板具备良好的厚度方向力学性能（避免层状撕裂）和抗大气腐蚀能力。
符号选择 ：
需厚度方向性能，最小断面收缩率 25%，故添加+Z25；
需抗大气腐蚀的热浸锌涂层，添加+Z；
基础钢种：选用结构钢 S355J2
最终钢名：S355J2+Z25+Z
该钢种满足桥梁对强度、低温韧性、厚度方向性能的要求，镀锌涂层可延长户外服役寿命。
场景示例2 汽车底盘冷冲压件（需冷作硬化与磷化前处理）
需求分析：汽车底盘部件需通过冷冲压成形，要求材料冷作硬化后强度达标，且表面状态适合后续磷化处理（需冷轧基底）。符号选择：
冷作硬化后最小抗拉强度 300MPa，添加+C300；且需冷轧基底，添加+CR。
基础钢种：选用冷成形用扁平材DC04。
最终钢名：DC04+CR+C300
冷轧状态（+CR）保证良好的冲压成形性，冷作硬化（+C300）提升强度，满足底盘部件的力学与加工要求。
需求分析：化工管道输送高温高压介质，要求钢管具备均匀的淬透性（保证整体力学性能一致）和耐酸碱腐蚀的表面涂层。
符号选择：
需整体淬透性，添加+H。
采用电解铬/氧化铬涂层（耐化学腐蚀），添加+CE。
基础钢种：选用13CrMo4-5
最终钢名：13CrMo4-5+H+CE
淬透性符号（+H）确保管道壁厚方向性能均匀，CE 涂层可抵抗介质腐蚀，适合化工环境使用。
需求分析：电机铁芯需低铁损、高磁导率，且需经退火消除应力以稳定磁性能，表面无需涂层（避免影响叠片效率）。
符号选择
基础钢种：选用电工钢 M400-50A（依据表 11，铁损 4.00W/kg，无取向）。
需软化退火消除应力，添加+A。
无需涂层，不添加符号。
基础钢种：选用电工钢 50W400
最终钢名：50W400+A
退火处理（+A）降低铁芯损耗，无涂层设计保证叠片时的紧密贴合，提升电机效率。