A514 Grade A - ASTM A514/A514M-2018

牌号	A514 Grade A
对应标准	ASTM A514/A514M-2018 焊接用经回火与淬火的高屈服强度合金钢板 Standard Specification for High-Yield-Strength, Quenched and Tempered Alloy Steel Plate, Suitable for Welding
归类	合金钢
性能	强度

A514 Grade A 化学元素成分含量(%)

	成分	C	Si	Mn	P	S	Cr	Mo	Ti ^①	Zr ^②	B
板厚t≤32mm(1.25in.)	最小值	0.15	0.4	0.8	-	-	0.5	0.18	-	0.05	-
板厚t≤32mm(1.25in.)	最大值	0.21	0.8	1.1	0.03	0.03	0.8	0.28	0.06	0.15	0.0025

① Ti may be present to protect the boron additions.
② Zr may be replaced by cerium. When cerium is added, the cerium/sulfur ratio should be 1.5 to 1 based upon heat analysis.

碳当量计算

A514 Grade A 机械性能

条件	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	断面收缩率 ψ %	硬度 HBW
板材;t≤20	淬火和回火	760~895	≥690	≥18	≥40	235~293
板材;20<t≤65	淬火和回火	760~895	≥690	≥18	≥40
板材;65<t≤150	淬火和回火	690~895	≥620	≥16	≥50

注：数据仅供参考！如有疑问，请填写"我要纠错"！