A709 Grade 50W - ASTM A709/A709M-2017

牌号	A709 Grade 50W
对应标准	ASTM A709/A709M-2017 桥梁用结构钢 Structural Steel for Bridges
归类	合金钢

A709 Grade 50W 化学元素成分含量(%)

	成分	C ^①	Si	Mn ^①	P ^②	S ^②	Cr	Ni	Cu	V
Type A	最小值	-	0.3	0.8	-	-	0.4	-	0.25	0.02
Type A	最大值	0.19	0.65	1.25	0.03	0.03	0.65	0.4	0.4	0.1

	成分	C ^①	Si	Mn ^①	P	S	Cr	Ni	Cu	V
Type B	最小值	-	0.15	0.75	-	-	0.4	-	0.2	0.01
Type B	最大值	0.2	0.5	1.35	0.03	0.03	0.7	0.5	0.4	0.1

① For each reduction of 0.01 percentage point below the specified maximum for carbon, an Increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50 %.
② A maximum phosphorus content or 0.04 % and a maximum sulfur content of 0.05 % are permitted for the following materials：structural shapes, Bars, Plates with widths up to and including 15 in. (380mm).

碳当量计算

A709 Grade 50W 机械性能

条件	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
棒材,板材; t≤100mm	≥485	≥345	（in 50mm） ≥21
型钢	≥485	≥345	≥21

注：数据仅供参考！如有疑问，请填写"我要纠错"！