F593 416 S41600 - ASTM F593-2017

牌号	F593 416
美国UNS	S41600
对应标准	ASTM F593-2017 不锈钢螺栓、六角螺钉和螺柱标准规范 Standard specification for stainless steel bolts, hex cap screws, and studs
归类	马氏体不锈钢

F593 416 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Mo ^①
最小值	-	-	-	-	0.15	12	-
最大值	0.15	1	1.25	0.06	-	14	0.6

① 由制造商选择添加元素。

碳当量计算

F593 416 机械性能

公称直径 inch 试样	热处理或状态	抗拉强度 σ_b ksi	屈服点 σ_s ksi	断后伸长率或延伸率 δ %	硬度 HBW
1/4 ~ 1-1/2 (全尺寸)	H	110~140	≥90		HR (C20~30)
1/4 ~ 1-1/2 (全尺寸)	HT	160~190	≥120		HR (C34~45)
1/4 ~ 1-1/2 (机加工)	H	≥110	≥90	≥18
1/4 ~ 1-1/2 (机加工)	HT	≥160	≥120	≥12

注1： “全尺寸”指的拉力测试试件是使用前的状态未经改变的完整的紧固件产品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.

近似对照表马氏体不锈钢

中国

中国台湾

日本

韩国

美国

国际标准组织

德国

法国

欧标

瑞典

英国

ISC

CNS

JIS

ASTM

UNS

ISO

数字牌号

DIN EN/DIN

W-Nr.

NF EN/NF

数字牌号

BS EN/BS

Y12Cr13
(Y1Cr13)

S41617

416

SUS 416

STS 416

416

S41600

X12CrS 13

4005-416-00-I

X12CrS 13

1.4005

Z12CF 13
Z11CF13

X12CrS 13

1.4005

2380

416S21

材料牌号对应供应商

告诉我在“材数库”看到，将给您优惠

上海三富金属集团有限公司

主营: 冷镦线材特殊钢钢带合金钢模具钢轴承钢弹簧钢齿轮钢冷墩钢冷拉钢

联系人：林先生移动电话： 13818300616/18601636665 电话：021-67600511/67600335 微信号：13818300616/18601636665 Email:

登陆后可见

钢棒、钢线、钢管、钢板、钢带、异形等

[询价]

注：数据仅供参考！如有疑问，请填写"我要纠错"！