Grade LCA J02504 - ASTM A352/A352M-2021

牌号	Grade LCA
美国UNS	J02504
对应标准	ASTM A352/A352M-2021 低温用铁素体及马氏体铸钢承压件 Steel Castings, Ferritic and Martensitic, for Pressure- Containing Parts, Suitable for Low-Temperature Service
归类	碳钢
标签	碳钢铸件

Grade LCA 化学元素成分含量(%)

成分	C ^①	Si	Mn ^①	P	S	Cr ^②	Ni ^②	Cu	Mo	V ^②
最小值	-	-	-	-	-	-	-	-	-	-
最大值	0.25	0.6	0.7	0.04	0.045	0.5	0.5	0.3	0.2	0.03

① 最大碳含量每减少0.01%，则最大锰含量增加0.04%，允许最大锰含量到1.1%
② 残余元素，Cr+Ni+V≤1%

碳当量计算

Grade LCA 机械性能

抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	断面收缩率 ψ %	冲击吸收能量 KV2 J
415~585	≥205 ⓐ	≥24 ⓑ	≥35	-32°C: ≥18

ⓐ Determine by either 0.2 % offset method or 0.5 % extension-under-load method.
ⓑ When ICI test bars are used in tensile testing as provided for in Specification A703/A703M, the gage length to reduced section diameter ratio shall be 4 to 1.