309C30 - BS 3100-1991

牌号	309C30
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	耐热不锈铸钢

309C30 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	-	-	-	-	-	22	10	-
最大值	0.5	2.5	2	0.05	0.05	27	14	1.5

碳当量计算

309C30 机械性能

热处理或状态	抗拉强度 σ_b	屈服点 σ_s	断后伸长率或延伸率 δ %	硬度 HBW	冲击吸收能量 KV2 J
N或N+T或QQ+T或WQ+T	540~690	≥320	≥16	152~207	≥30

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐热铸钢和耐热合金铸件

中国

中国台湾

日本

韩国

美国

国际标准组织

德国

法国

俄罗斯

英国

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ZG40Cr25Ni12Si2

C53881

SCH 13

SCH 13X

HRSC 13

HHtypeⅡ

J93503

GX40CrNiSi25-12

1.4837

GX40CrNiSi25-12

≈40Х24Н12СЛ

309C30

2 近似对照表耐热铸钢和耐热合金铸件

日本	美国		德国		俄罗斯	英国
JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	GOST	BS EN/BS
SCH13A SCH17	HH	J93503	G-X40CrNiSi25 21	1.4837	40Х24Н12Л	309C30