332C15 - BS 3100-1991

牌号	332C15
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	不锈铸钢

332C15 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo	N
最小值	-	-	-	-	-	21	4	1.75	0.1
最大值	0.08	1.5	1.5	0.04	0.04	27	7	3	0.25

碳当量计算

332C15 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
ST(1110°C min)	≥640	1% proof stress Rp1.0 min ≥430	≥30	≥25

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

注：数据仅供参考！如有疑问，请填写"我要纠错"！