347C17 - BS 3100-1991

牌号	347C17
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	奥氏体不锈铸钢有磁性

347C17 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	更多
最小值	-	-	-	-	-	18	9	Nb:8C~1
最大值	0.08	1.5	2	0.04	0.04	21	12	Nb:8C~1

碳当量计算

347C17 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
ST(1000°C~1100°C)	≥480	1% proof stress Rp1.0 min ≥215	≥22

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	美国	德国		法国	英国
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG0Cr18Ni9Ti	SUS21	CF8C	G-X7CrNiNb 18 9	1.4552	Z6CNNb18.10M	347C17

2 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		法国	俄罗斯	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9Ti	SCS21	CF8C	J92710	G-X5CrNiNb18 9	1.4552	Z4CNNb19.10M	08Х18Н9Т	347C17

注：数据仅供参考！如有疑问，请填写"我要纠错"！