410C21 - BS 3100-1991

牌号	410C21
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	不锈钢铸钢

410C21 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu ^①
最小值	-	-	-	-	-	11.5	-	-
最大值	0.15	1	1	0.04	0.04	13.5	1	0.3

①残余元素

碳当量计算

410C21 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
AH+T或OQ+T(T at 750°C max)	≥540	≥370	≥15

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐蚀铸钢（不锈钢铸件）

中国

中国台湾

日本

韩国

美国

国际标准组织

德国

法国

俄罗斯

瑞典

英国

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG15Cr12

C54100

SCS 1

SCS 1X

SSC 1

CA15

J91150

GX12Cr12

1.4011

Z12C13M

15Х13Л

2302

410C21

2 近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	美国	德国		法国	俄罗斯	英国
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG1Cr13	SUS1	CA15	G-X8Cr14 X15Cr13	1.4008 1.4024	Z12C13M	15Х13Л	410C21

3 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		法国	俄罗斯	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG1Cr13	SCS1	CA15	J91150	G-X7Cr13 G-X10Cr13	1.4001 1.4006	Z12C13M	15Х13Л	410C21

注：数据仅供参考！如有疑问，请填写"我要纠错"！