AM1 - BS 3100-1991

牌号	AM1
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
标签	高磁导率碳钢铸钢

AM1 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr ^②	Ni ^②	Cu ^②	Mo ^②	其他合计
最小值	-	-	-	-	-	-	-	-	-	-
最大值	0.15	0.6	0.5	0.05	0.05	0.3	0.4	0.3	0.15	0.8

其他单个或其他合计化学成分包括表中未指定值的化学成分。只有在假定存在或在常规分析中，且有迹象表明其成分将超过规定值的情况下，才应进行分析。

①碳含量每降低0.01%，最大锰含量则增加0.04%，允许最大锰含量到1.1%
②残余元素。

碳当量计算

AM1 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
A或N	340~430	≥185	≥22

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似对照表结构、压力容器和工程钢

日本	美国	国际标准组织	德国	法国	欧标		俄罗斯	英国
JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	数字牌号	GOST	BS EN/BS
SC37	Gr.N1	20-40	GS38	20-40M	C18D	1.0416	15L	AM1