X1NiCrMoCu25-20-5 1.4539 - NF EN 10088-2-2005

牌号	X1NiCrMoCu25-20-5
	1.4539
对应标准	NF EN 10088-2-2005 普通用途不锈钢板和钢带的交货技术条件 Part2:Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
归类	奥氏体不锈钢
标签	标准等级

X1NiCrMoCu25-20-5 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N
最小值	-	-	-	-	-	19	24	1.2	4	-
最大值	0.02	0.7	2	0.03	0.01	21	26	2	5	0.15

◎ 未经买方同意，不得随意向钢中添加表中未列的元素，冶炼精加工除外。采取一切必要措施以防在废钢和生产原料中带入这些元素，因为其会削弱钢的机械性能，降低钢的适用性。

◎ 在询价和订购时可商定更严格的碳含量范围。

碳当量计算

X1NiCrMoCu25-20-5 机械性能

条件	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
冷轧带钢：T ≤ 8mm	+AT	530~730	( t ) Rp0.2：≥ 240①③ Rp1.0：≥ 270①② ③	( t ) T＜3mm：≥35③④ T ≥ 3mm：≥35③⑤	-
热轧带钢：T ≤ 13.5mm	+AT	530~730	( t ) Rp0.2：≥ 220①③ Rp1.0：≥ 260①② ③	( t ) T＜3mm：≥35③④ T ≥ 3mm：≥35③⑤	（T＞10mm） I：≥ 100；t：≥60
热轧中厚板：T ≤ 75mm⑥	+AT	520~720	( t ) Rp0.2：≥ 220①③ Rp1.0：≥ 260①② ③	( t ) T＜3mm：≥35③④ T ≥ 3mm：≥35③⑤	（T＞10mm） I：≥ 100；t：≥60

◎ T-厚度；l-纵向; t-横向
◎ +A=软化退火；+QT=淬火及回火；+P=沉淀硬化；+AT=固溶退火；+SR=消除应力

① 对于连续热轧产品，可在询价和订购时商定Rp0.2(即表中σs)的最小值提高20MPa，Rp1.0的最小值提高10MPa。
② 仅作指导
③ 如果在轧制宽度<300mm的情况下，采用纵向试验件，最小值减小如下:屈服强度-15MPa，恒定标距的延伸率-5%，比例标距延伸率-2%。
④ T＜3mm时适用于标距为80mm、宽度为20mm的试件。也可以使用标距为50mm、宽度为12.5mm的试件。
⑤ T ≥3mm时适用于标距为5.65√S的试件。
⑥ T＞75mm，可以协商机械性能。
* 交货条件下有抗晶间腐蚀; 致敏条件下有抗晶间腐蚀（根据EN ISO 3651-2进行测试）。

交付条件下在高温下的最小屈服强度

Material designation		Heat treatment condition	Minimum 0.2%-proof strength,MPa at a temperature (in°C) of:										Minimum 1%-proof strength,MPa at a temperature (in°C) of:
Name	Number	Heat treatment condition	100	150	200	250	300	350	400	450	500	550	100	150	200	250	300	350	400	450	500	550
X1NiCrMoCu25-20-5	1.4539	+AT	205	190	175	160	145	135	125	115	110	105	235	220	205	190	175	165	155	145	140	135

符合本欧洲标准的产品热处理指南

Material designation		Hot forming		Heat treatment symbol	Solution anneailing
Name	Number	Temperature ℃	Type of cooling	Heat treatment symbol	Temperature①②③ ℃	Type of cooling④
X1NiCrMoCu25-20-5	1.4539	1150 to 850	air	+AT	1060 to 1140	water,air

◎ Temperature of solution annealing shall be agreed for simulated heat-treated test pieces.
① Solution annealing may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained.
② If heat treatment is carried out in a continuous furnace, the upper part of the range specified is usually preferred, or even exceeded.
③ Lower end of the range specified for solution annealing should be aimed at the heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing, a temperature of 980℃ is adequate as a lower limit for Mo-free steels, a temperature of 1000℃ for steels with Mocontents up to 3 % and a temperature of 1020°C for steels with Mo contents exceeding 3 %.
④ Cooling sufficiently rapidly in order to avoid the occurrence of intergranular corrosion as defined in EN ISO 3651-2.

X1NiCrMoCu25-20-5 对应不同标准

1	EN 10088-1-2005 不锈钢第1部分:不锈钢的清单
	X1NiCrMoCu 25-20-5 1.4539
2	EN 10296-2-2005 机械工程和一般工程用焊接圆钢管.交货技术条件.第2部分:不锈钢
	X1NiCrMoCu25-20-5 1.4539
3	EN 10253-4-2003 对接焊管道接头.具有特殊检验要求的锻制奥氏体和铁素体－奥氏体(二相)不锈钢
	X1NiCrMoCu25-20-5 1.4539
4	EN 10250-4-1999 一般工程用途的自由锻钢锻件:不锈钢
	X1NiCrMoCu 25-20-5 1.4539
5	ISO TS 15510-2003 技术规范不锈钢-化学成分
	X1NiCrMoCu25-20-5
6	EN 10088-3-2005 不锈钢第3部分：一般用途的半成品，钢棒，轧制线材和型钢的交货条件
	X1NiCrMoCu 25-20-5 1.4539
7	EN 10088-3-2014 不锈钢 - 第3部分：半成品，棒材，杆材，线材，型材和光亮产品的一般用途耐腐蚀钢的交货技术条件
	X1NiCrMoCu25-20-5 1.4539
8	ISO 15510-2014 技术规范不锈钢-化学成分
	X1NiCrMoCu25-20-5 4539-089-04-I
9	ISO 9328-7-2018 不锈钢承压扁钢制品
	X1NiCrMoCu25-20-5
10	DIN EN 10088-3-2014 不锈钢-半成品、棒材、杆材、线材、型材及光亮产品交货技术条件
	X1NiCrMoCu25-20-5 1.4539
11	DIN EN 10270-3-2012 机械弹簧钢丝—第3部分：不锈弹簧钢丝
	X1NiCrMoCu25- 20-5 1.4539
12	ISO 683-18-2014 热处理钢、合金钢和易切削钢 -- 第18部分：光面钢制品
	X1NiCrMoCu25-20-5 4539-089-04-I
13	NF EN 10088-2-2005 普通用途不锈钢板和钢带的交货技术条件
	X1NiCrMoCu25-20-5 1.4539
14	NF EN 10088-1-2005 不锈钢 - 第1部分：不锈钢清单
	X1NiCrMoCu25-20-5 1.4539
15	NF EN 10028-7-2008 压力容器用不锈钢扁平产品
	X1NiCrMoCu25-20-5 1.4539
16	NF EN 10296-2-2005 机械和一般工程用焊接圆钢管-交货技术条件-第2部分:不锈钢管
	X1NiCrMoCu25-20-5 1.4539
17	NF EN 10028-7-2000 压力容器用不锈钢扁平产品
	X1NiCrMoCu25-20-5 1.4539

注：数据仅供参考！如有疑问，请填写"我要纠错"！