牌号 B2
对应标准 BS 3100-1991
一般工程用铸钢件
Specification for Steel castings for general engineering purposes
归类 铸钢
标签 高温用合金钢铸钢
B2 化学元素成分含量(%)
成分 C Si Mn P S Cr Ni Cu Mo
最小值 - - 0.5 - - 1 - - 0.45
最大值 0.2 0.6 0.8 0.04 0.04 1.5 0.4 0.3 0.65
①残余元素。
B2 机械性能
热处理或状态
抗拉强度
σb
Mpa
屈服点
σs
Mpa
断后伸长率或延伸率
δ
%
冲击吸收能量
KV2
J
N+T或OQ+T或WQ+T(T 700°C max) ≥480 ≥280 ≥17 ≥30
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
B2 对应不同标准
1 JIS G 7401-2000 冷锻及冷轧挤压用钢
2 ISO 4954-1993 冷镦和冷挤压用钢
3 ASTM B103/B103M-2019 磷青铜板、薄板、带材和轧制棒材
4 ASTM A485-2014 高淬透性耐磨轴承钢的技术规范
5 ASTM A485-2017 高淬透性耐磨轴承钢的技术规范
6 BS 3100-1991 一般工程用铸钢件
B2
注:数据仅供参考!如有疑问,请填写"我要纠错"!