ENiCrMo-5A Material Data

Name: ENiCrMo-5A Material Data
Creator: 材数库 Caishuku
License: https://www.caishuku.com/ai-license.html

材数库 Caishuku

基本信息

牌号	ENiCrMo-5A
	W80002
对应标准	AWS A5.13/A5.13M-2010 堆焊焊条规范保护金属电弧焊 Specification for Surfacing Electrodes for Shielded Metal Arc Welding
归类	合金钢
标签	镍基堆焊焊条
说明	Characteristics. Undiluted weld metal deposited by ENiCrMo-5A electrodes is a solid-solution-strengthened alloy with relatively low weight-percent carbide phase produced through secondary hardening. The resultant deposit is tough and work hardenable. Deposits have the ability to retain hardness up to 1400°F [760°C]. Deposits are machinable with high-speed tool bits and have excellent resistance to high-temperature wear and impact. Applications. These electrodes are used to rebuild and repair hot extrusion dies, hot forging dies, sizing punches, hot shear blades, guide rolls, tong bits, blast furnace bells, etc.

化学成分

ENiCrMo-5A 化学元素成分含量(%)

成分	Fe	C	Si	Mn	P	S	Cr	Mo	W	V	其他合计	更多
最小值	4	-	-	-	-	-	14	14	3	-	-	Ni:余量
最大值	7	0.12	1	1	0.03	0.03	18	18	5	0.4	1	Ni:余量

其他单个或其他合计化学成分包括表中未指定值的化学成分。只有在假定存在或在常规分析中，且有迹象表明其成分将超过规定值的情况下，才应进行分析。

注：数据仅供参考！如有疑问，请填写"我要纠错"！

版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。

摘要 / Summary

ENiCrMo-5A 材料牌号数据，其他名称/统一牌号：W80002，对应标准：AWS A5.13/A5.13M-2010，主要化学成分：Fe 4–7%，C ≤0.12%，Si ≤1%，Mn ≤1%，P ≤0.03%，S ≤0.03%，Cr 14–18%，Mo 14–18%，W 3–5%，V ≤0.4%，其他合计 ≤1%，Ni:余量。数据来源：材数库 Caishuku.com。

推荐引用：材数库 Caishuku Material Database，《ENiCrMo-5A 材料牌号数据》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxMTUzMzk=