ECoCr-B Material Data

Name: ECoCr-B Material Data
Creator: 材数库 Caishuku
License: https://www.caishuku.com/ai-license.html

材数库 Caishuku

基本信息

牌号	ECoCr-B
	W73012
对应标准	AWS A5.13/A5.13M-2010 堆焊焊条规范保护金属电弧焊 Specification for Surfacing Electrodes for Shielded Metal Arc Welding
归类	合金钢
标签	钴基堆焊焊条
说明	Characteristics. Weld metal deposited by ECoCr-B electrodes is similar in composition to ECoCr-A deposits except for a slightly higher carbide content (approximately 16%). The alloy also has a slightly higher hardness coupled with better abrasive and metal-to-metal wear resistance. Impact and corrosion resistance are lowered slightly.Deposits can be machined with carbide tools. Applications. ECoCr-B electrodes are used interchangeably with ECoCr-A. Choice will depend on the specific application.

化学成分

ECoCr-B 化学元素成分含量(%)

成分	Fe	C	Si	Mn	P	S	Cr	Ni	Mo	W	其他合计	更多
最小值	-	1	-	-	-	-	25	-	-	7	-	Co:余量
最大值	5	1.7	2	2	0.03	0.03	32	3	1	9.5	1	Co:余量

其他单个或其他合计化学成分包括表中未指定值的化学成分。只有在假定存在或在常规分析中，且有迹象表明其成分将超过规定值的情况下，才应进行分析。

注：数据仅供参考！如有疑问，请填写"我要纠错"！

版权说明：
⑴ 本网站的所有内容（包括但不限于文字、图片、音频、视频等）均受到版权保护，版权归本网站所有；
⑵ 未经授权，禁止以任何形式转载、复制、传播或用于其他商业用途；
⑶ 如需使用本网站内容，请提前获得授权。

材料与专利钢号免责声明：
⑴ 本平台所收录的部分材料牌号为企业专利钢号或专有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标准钢号；
⑵ 相关化学成分、力学性能及适用范围以专利文件、权利人公开资料或供方技术文件为准；
⑶ 平台所展示信息仅用于材料检索、工程参考及技术对比，不构成等同、替代或采购依据。

摘要 / Summary

ECoCr-B 材料牌号数据，对应标准：AWS A5.13/A5.13M-2010，主要化学成分：Fe ≤5%，C 1–1.7%，Si ≤2%，Mn ≤2%，P ≤0.03%，S ≤0.03%，Cr 25–32%，Ni ≤3%，Characteristics. Weld metal deposited by ECoCr-B electrodes is similar in composition to ECoCr-A deposits except for a slightly higher carbide content (approximately 16%). The alloy als。

推荐引用：材数库 Caishuku Material Database，《ECoCr-B 材料牌号数据》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxMTUzMzU=

ECoCr-B 的供应商信息由材数库认证企业提供。本页面展示的企业均为材数库认证供应商，企业名称、联系人、联系方式、主营产品及供货信息由企业提交，经材数库审核后发布并持续维护。