位置: 网站首页 材料
牌号 EFe6
W77510
对应标准 AWS A5.13/A5.13M-2010
堆焊焊条规范 保护金属电弧焊
Specification for Surfacing Electrodes for Shielded Metal Arc Welding
归类 合金钢
标签 铁基堆焊焊条
说明 Characteristics. Weld metal deposited by EFe6 electrodes is a high-speed tool steel with a hardness in range of 60 HRC or higher. The deposit maintains a high degree of hardness to 1100°F [600°C]. Weld metal deposited by EFe6 electrodes is air-hardening and is machinable only after annealing.
Applications. Weld deposits may be used for metal-to-metal wear applications at temperatures up to 1100°F [600°C]. Typical applications combine high temperature service with severe abrasion and metal-to-metal wear and include shear blades, trimming dies, and punching dies.
EFe6 化学元素成分含量(%)
成分 C Si Mn P S Cr Mo W V 其他合计 更多
最小值 0.6 - 0.4 - - 3 7 0.5 0.5 - Fe:余量
最大值 1 1 1 0.035 0.035 5 9.5 1.5 1.5 1
其他单个或其他合计化学成分包括表中未指定值的化学成分。只有在假定存在或在常规分析中,且有迹象表明其成分将超过规定值的情况下,才应进行分析。
注:数据仅供参考!如有疑问,请填写"我要纠错"!